Erna Frida, Ratnawulan, Nurdin Bukit, Bunga Fisikanta Bukit, Ahmad Taufiq, Agus Wedi Pratama, Istiqomah Rahmawati, Ferry Rahmat Astianta Bukit
Superhydrophilic and self-cleaning coatings have attracted significant interest across various industries. While multiple approaches exist for creating such coatings, biomass is an environmentally friendly and cost-effective option such as palm oil boiler ash (OPBA). This study investigates the development of superhydrophilic cotton fabric coating and self-cleaning by combining SiO2-contained OPBA (SiO2-OPBA) with TiO2. SiO2-OPBA was synthesized from OPBA by calcining OPBA at 500 °C for 5 h then milled in a Ball Mill. Furthermore, OPBA was coprecipitated to produce dominant SiO2. Meanwhile, TiO2 was prepared using TiCl4 by sol-gel method. SiO2-OPBA and TiO2 are combined with the addition of maleic acid as a compatibilizer and sodium hypophosphite as a catalyst. Coating on the fabric using the dip-pad-dry-cure method. Characterization of coated fabrics by SEM, FTIR, contact angle testing, and self-cleaning activity. SEM characterization shows that SiO2/TiO2 agglomerates can fill the voids, preventing foreign particles from penetrating the fabric structure and limiting their deposition on the outer surface. No significant changes were observed from FTIR of coated fabrics compared to pure cotton fabrics, probably due to overlapping peaks of coating materials and cellulose bandwidth. Carbonyl esters were the major component in all samples. A significant reduction in the contact angle was observed after coating compared with the initial cotton fabric (63°). The Ti1Si1 and Ti1Si2 coated fabrics reached a contact angle of 0°. The presence of SiO2 in OPBA enhances the surface area of TiO2 particles, thereby improving the adsorption of stains and the overall self-cleaning mechanism. © 2024 The Authors
Department of Physics, Faculty of Mathematics and Natural Sciences, Universitas Sumatera Utara, Sumatera Utara, Medan, Indonesia; Department of Physics, Faculty of Mathematics and Natural Sciences, Universitas Negeri Padang, Sumatera Barat, Padang, Indonesia; Department of Physics, Faculty of Mathematics and Natural Sciences, Universitas Negeri Medan, Medan, Indonesia; Faculty of Science and Technology, Universitas Quality Berastagi, Karo, Sumatera Utara, Indonesia; Department of Physics, Faculty of Mathematics and Natural Sciences, Universitas Negeri Malang, Indonesia; Department of Chemistry, Faculty of Science and Data Analytics, Institut Teknologi Sepuluh Nopember, Surabaya, Indonesia; Department of Chemical Engineering, Faculty of Engineering, University of Jember, Indonesia; Department of Electrical Engineering, Faculty of Engineering, Universitas Sumatera Utara, Sumatera Utara, Medan, Indonesia